==Knife Sharpening - An aide Memoire==
Starting Point: Shape of knife already done and rough bevel created, double-bevel shape already created.
This page is not finished and are just rough notes based on the [[Workshops/bladesmithing|bladesmithing]] workshop
===General Notes
*Blades can be sharpened with an included angle anywhere from 7 degrees (razor blade) to 45 degrees (axe head). Finer edges are sharper but weaker so they dull faster, wider edges are less sharp but much more robust and will last much longer before resharpening.
*Desired sharpness depends on what you're cutting, not much point going above 1000/1500 (and strop) with wood
Line 14:
* Note on grit grades, not all 1000-grit stones are equal. Stones made from a hard material (e.g. diamond) will behave as if they're coarser than the grit number would suggest, stones made from a soft material (e.g. F3 stone) will behave as if they're finer than the grit number would suggest
*All Stones used wet- to aid lubrication and cleaning off swarf, use spray bottle to regularly re-wet while using.
**Diamond stones are stored dry but should be frequently wetted while in use
**Water stones:
***
***Only use water. Certain stones can be used with oil but then can never be used with water again.
***Water stones may not be completely flat from previous use (dished).
**English stone can be kept dry but needs to be soaked in water for half an hour before use.
**F3 stones don't need soaking and should be stored dry but still need to be wetted regularly while in use.
*Both Water and English stones need even more care on push stroke to prevent nicking stones.
*Use the full length of the stones but take care not to run off the ends, longer strokes both work faster and help prevent uneven wear on the stones.
===General Process===
*Choose an angle and hold it as stable as you can. Can be helpful to move entire upper body rather than just arms. Do not "Roll" the knife over the stone. Angle might get slightly steeper as you go up the grits if you're aiming for a prismatic grind but is usually constant.
*Firm Pull stroke on stones, very light push stroke (to prevent nicking stones), Sharpening on the push stroke is a thing that can be done and it actually results in a (slightly) nicer edge than pull strokes if it's done perfectly, but it's much easier to get wrong and damage both blade and stones so it's strongly discouraged on the lab-owned stones
*Should only have to do 400 Grit when first shaping edge, unless you've badly nicked the blade
*Clean Knife between grits - otherwise previous swarf can scratch blade - water and wipe
Line 52 ⟶ 54:
*Burr probably too small to be felt
===4000 F3 (triple fine)
*Polishing the cutting edge, razor sharp at this point and usable even in quite soft materials
*Use only light pressure on both strokes
Line 65 ⟶ 67:
====Stropping 30000 grit====
*Puts a mirror polish on the edge
*Result under microscope: Definite shine, like mirror
*Only pull strokes on leather strop, 30/40 on each side with stropping compound
*Hard-backed strops make it easier to hold proper angle, flexible strops will round-over the edge if not used very carefully
===Time Taken
*30 mins for
*High-end tool steel - double numbers above
*Super-steels and ceramic blades are not sharpenable by this process and require diamond lapping compounds and suitable pads.
==Resharpening Blade==
|